SiMT
Southeastern Institute of Manufacturing and Technology
RP CAPABILITIES
ABOUT SIMT
JONATHAN WILKE
Jonathan Wilke
Jonathan Wilke has worked as lead RP technician in the SiMT Rapid Prototyping Center since 2007.
 
Prior to joining SiMT, he served as a product designer at ESAB Welding and Cutting.
 
He holds two engineering technology degrees from Florence Darlington Technical College (FDTC) in Florence, South Carolina.
 
Jonathan is available to assist with your company's outsourcing and RP overflow needs.
  
Jonathan Wilke 
Email or 843 413-2747
Join Our Mailing List 
WHAT'S OPEN AT SiMT RAPID PROTOTYPING CENTER 
Accura® 25 Plastic on the Viper™ Pro SLA® 
Accura® 60 Plastic on the Viper™ Pro SLA®
DuraForm® PA on the Sinterstation® Pro 230 
LaserForm™ A6 Metal on the Sinterstation® HiQ™ SLS®
VisiJet® SR 200 Plastic on the InVision® XT 3-D Modeler
Dear Nadra,

Did you know LaserForm A6 material produces functional metal tooling in less than four days? That's compared to the 11-day average needed to prepare traditional tooling inserts! So, if you're looking to create metals parts quickly, give us a call. And, if you're looking for materials that simulate the properties and aesthics of polypropylene, polycarbonate and/or nylon, remember -- our machines are standing by to assist with your rapid product development projects.

For more information about creating complex metal parts, contact Jonathan Wilke or visit our website. 
 
Accura® 25 Plastic 
Accura 25Appearance: White
Tensile Strength: 38 MPa
Tensile Modulus: 1,590-1,660 MPa
Elongation at Break (%): 13-20%
Flexural Modulus: 1,380-1,660 MPa
Heat Deflection @ 66 PSI: 58-63 C
Hardness: Shore D 80
Download Accura 25 Datasheet
 
Accura® 60 Plastic 
Accura 60Appearance: Clear
Tensile Strength: 58-68 MPa
Tensile Modulus: 2,690-3,100 MPa
Elongation at Break (%): 5-13%
Flexural Modulus: 2,700-3,000 MPa
Heat Deflection @ 66 PSI: 53-55 C
Hardness: Shore D 86
Download Accura 60 Datasheet
 
DuraForm® PA 
Duraform PAAppearance: White
Tensile Strength: 43 MPa
Tensile Modulus: 1,586 MPa
Elongation at Break (%): 14%
Flexural Modulus: 1,387 MPa
Heat Deflection @ 0.45 MPa: 180 C
Hardness: Shore D 73
Download DuraForm PA Datasheet
 
LaserForm™ A6 Metal 
LaserForm A6Appearance: Metal
Tensile Strength: 610 MPa
Young's Modulus: 138 GPa
Elongation (%): 2-4%
Hardness: Rockwell C 10-20 (polished)
Hardness: Rockwell C 39 (heat treated)
Download LaserForm A6 Datasheet
 
VisiJet® SR 200 Plastic
VisiJet SR 200Composition: Acrylic
Appearance: Translucent White
Tensile Strength: 34 MPa
Tensile Modulus: 1772 MPa
Flexural Modulus: 1,786 MPa
Flexural Strength: 52 MPa
Download Accura 60 Datasheet
 
Contact RPC at SiMT
Jonathan Wilke, Rapid Prototyping Center
Email Jonathan
Southeastern Institute of Manufacturing and Technology
1951 Pisgah Road, Florence, SC 29502
(843) 413-2747 | www.simt.com
SiMT Rapid Prototyping Center 
The mission of the Southeastern Institute of Manufacturing and Technology (SiMT) is to provide customers with strategic training and manufacturing technology solutions that maximize workforce productivity in advanced manufacturing environments. In doing so, the SiMT Rapid Prototyping Center offers the latest RP technologies in support of industrial design, product development, rapid prototyping and manufacturing throughout the United States. For more information, email Jonathan Wilke.
www.simt.com

Forward email

This email was sent to nadra_angerman@hotmail.com, by jonathan.wilke@simt.com.
For more information contact Angerman Communications Group at: www.angerman.com.

Angerman Communications Group | P.O. Box 70219 | Seattle | WA | 98127